Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment
has a high maximum use temperature (800°C continuous, 1000°C peak).
No longer is it necessary to staff a ceramic specialist with high
temperature kilns or specialized diamond grinding equipment.
Main Properties of Machinable Glass Ceramic
| ITEM | UNIT | MGC |
| Type | - | Glass Ceramic |
| Density | g/cm3 | 2.55 |
| Color | - | white |
| Water Absorption | % | 0 |
| Young Modulus | Gpa | 65 |
| Vickers Hardness | Gpa | - |
| Compressive Strength | Mpa | 500 |
| Flexural Strength | Mpa | 100 |
| Thermal Conductivity | W/m.K | 1.70 |
| Thermal Shock Resistance | Δ(°C) | 25 - 100 |
| Max. Working Temp. | °C | 1000 |
| Volume Resistivity | Ω ·cm | 10^16 |
| Dielectric Constant | - | 6.02 |
| Dielectric Strength | kV/mm | 40 |
Industrial Ceramic Intriduction
has a high maximum use temperature (800°C continuous, 1000°C peak).
No longer is it necessary to staff a ceramic specialist with high
temperature kilns or specialized diamond grinding equipment.
Main Properties of Machinable Glass Ceramic
ITEM | UNIT | MGC |
Type | - | Glass Ceramic |
Density | g/cm3 | 2.55 |
Color | - | white |
Water Absorption | % | 0 |
Young Modulus | Gpa | 65 |
Vickers Hardness | Gpa | - |
Compressive Strength | Mpa | 500 |
Flexural Strength | Mpa | 100 |
Thermal Conductivity | W/m.K | 1.70 |
Thermal Shock Resistance | Δ(°C) | 25 - 100 |
Max. Working Temp. | °C | 1000 |
Volume Resistivity | Ω ·cm | 10^16 |
Dielectric Constant | - | 6.02 |
Dielectric Strength | kV/mm | 40 |
Aluminium Oxide, Al2O3 is the most widely applied and cost
effective technical ceramic material. It offers a combination of
superior mechanical strength and electrical properties, wear
resistance and corrosion resistance. The maximum working
temperature is up to 1700 °C with relatively high thermal
conductivity. It is also an electrically insulating material with a
high electrical resistivity. The good corrosion resistance makes it
insoluble in water and slightly soluble in strong acid and alkaline
solution.
Company Introduction
Mingrui ceramic manufacture and provides alumina ceramic components
for a wide range of application like Mechanical Equipment,
Electronic & Electrical, Oil Drilling, Medical, Chemical Industry
etc. According to actual application and customer's requirement,
the purities vary from 95%-99.7% and the forming methods will be
different. The forming methods applied in our plant include dry
pressing, isostatic pressing, injection moulding, extrusion
moulding. With experienced engineers and talented workers, we are
confident to offer high quality, high precision, complex components
for customers worldwide.
Product Description
Precision Ceramics has years of experience designing and developing
technical ceramic solutions for a wide variety of applications and
industries. Anti-dirty Industrial Ceramic Parts Petroleum Industry
Equipment. We offer this expertise to all of our customers to
ensure the best design and materials are chosen for their specific
application and needs. Anti-dirty Industrial Ceramic Parts
Petroleum Industry Equipment, Typically, our custom technical
ceramic components and parts we supply are used for one of three
main reasons:
Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment
High temperature ceramics – crucibles, nozzles, lasers,
furnace/kiln fixtures
Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment
Wear and corrosion resistant ceramics – plates, housings, gages,
caps/lids
Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment
Electrical insulation ceramics – contact blocks, standoffs,
fasteners, spacers
Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment
Precision Ceramics is one of the world’s premiere technical ceramic
suppliers – contact us to see what technical ceramics we can create
for you.
Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment
| Product Name | Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment |
| Material | Alumina Ceramic or zirconia ceramic |
| Color | white or black or customed |
| Standard | according the request of customer |
| Grade | first class |
| Brade | Rock |
| Thread | coarse, fine |
| Used | Anti-dirty Industrial Ceramic Parts Petroleum Industry Equipment |
Machining process
Raw materials-Molding process - Sintering - Machining & Grinding -
Quality InspectorMingrui ceramic parts property| · Flexural strength | · Chemical resistance | · Electrical insulation | · Corrosion resistance | · Dielectric strength |
| · Wear resistance | · Temperature resistance | · Thermal conductivity | · High voltage | · Hardness... |
Ceramic materials(include but not limited belows)
· 95%--99.99% Alumina (Al2O3) · Silicon Carbide · Silicon Nitride · TTZ: Magnesia partially stabilized Zirconia (ZrO2)
· YTZP: Yttria partially stabilized Zirconia (ZrO2) · ZDY: Yttria fully stabilized Zirconia (ZrO2)...
|
Al 2O 3 | ZrO2/Y2O3 | ZrO2/MgO | MgO | SiC | Si3N4 Reaction sintered | Si3N4 Hot pressed | ALN |
| Physical properties | | | | | | | | |
| Density (g/cm3) | 3,9 | 5,9 | 5,75 | 3,58 | 3,2 | 3,27 | 3,29 | 3,26 |
| Molecular weight (g/mole) | 102 | - | - | 40,4 | 40,1 | 140 | 140 | 41 |
| Maximum service temperature air (°C) | 1700- 1800 | 1500 | 1000 | 2200 | 1500 | 1200- 1500 | 1100- 1600 | 1000- 1800 |
| Mechanical properties | | | | | | | | |
| Hardness (Mohs) | 9 | - | - | 5,5 | 9 | - | - | 7 |
| Modulus of elasticity (GPa) | 300-400 | 200 | 200 | 250-300 | 420 | 170-220 | 280-310 | 318 |
| Poisson's ratio | 0,25 | - | - | 0,18 | 0,14 | 0,25-0,26 | 0,27 | 0,25 |
| Fracture toughness (MPa.m1/2) | 2-3 | 7-13 | 6-10 | - | 2,5-3,5 | 3,5-5 | 6,1 | 4,5 |
| Electrical properties | | | | | | | | |
| Dielectric constant | 9-10 | - | - | 9-10 | - | 10 | 10 | 9,2 |
| Electrical resistivity at 20°C (Ohm.cm) | >10 14 | 10 13-10 14 | >10 10 | - | 10 2-10 6 | >10 7 | 10 12- 10 15 | >10 14 |
| Dielectric strength (kV/mm) | 10-20 | 9 | 2-10 | - | - | - | - | 15 |
| Thermal properties | | | | | | | | |
| Specific heat (J/K/kg) | 900 | 400-500 | 420 | 870-880 | 750 | 690 | 680-800 | 800 |
| Thermal conductivity (W/m/K) at 20°C | 26-35 | 2,2-3,2 | 1,5-2,5 | 40-50 | 63-155 | 9-30 | 15-43 | 180 |
| Coefficient of thermal expansion ( 10-6) from 20 to 1000°C | 8-9 | 10-11 | 5-16 | 10-13 | 4-5 | 3 | 3,3 | 4,4-5,3 |
| Melting point (°C) | 2050 | 2590 | - | 2800 | 2500 | 1900 | 1900 | 2200 |
Customization & Machining Service:
As a ceramic parts manufacturer,us offer a wide of the ceramic
specification,and customized&machinables.
Get a Quote On Your
Customized Now!! or up a files by
EMAIL.
Our Custom Capabilities:
1.High Purity Martoxid Powder
2.OEM Support, More Than 10 Technicians With 5-Year R&D
Experience
3.35000 ㎡workshop, annual output could reach hundred million
pieces.
4.All crafts are inspected strictly based on drawings,checked each
month.
5.Best Service And Quick Delivery Via Fedex,DHL,UPS,TNT Etc. | | | Technical reference of manufacture | | Dimensional accuracy | Up to 0.001mm | | Concentricity | Up to 0.003mm | | Parallelism | Up to 0.002mm | | The inner hole tolerance | The minimum 0.005mm | | Straight flute | The narrowest 0.1x100mm | | The thickness of the size | Minimum to 0.02mm | | The screw thread | Minimum internal thread M2 | | Cylindricity | Up to 0.004mm | | The linear tolerance | Up to 0.001mm | | The smallest aperture | The minimum 0.07mm | | Precision process | CNC maching,grinding,lapping | | Surface finish | Glazed,polishing or metallized
|
|
FAQ
Q: Are you trading company or manufacturer ?
A: We are factory.
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is
15-20 days if the goods are not in stock, it is according to
quantity.
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay
the cost of freight.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 30%
T/T in advance ,balance before shippment.
If you have any other question, pls feel free to contact us .